Product Description
0Cr23Al5 FeCrAl Alloy Thermal Spray Wire used in arc spraying
Producrs Introduction:
FeCrAl is a high-resistivity iron-chromium-aluminium alloys for use up to 1400º C (2550º F). With the well-bonding coating and high temperature oxidation resistance. So they can use in variety of industry.
They can equivalent to: TAFA Alcro PMET731
Typical Uses and Applications
Applications where good corrosion and oxidation Resistance is required
Applications for wear resistance such as erosion and abrasion
Machine element repair and restoration
Resistance to chloride-ion attack in marine environments
As a replacement for hard chrome plating
Bond coats in high-temperature coating systems
l Protective coatings against sulphur-containing atmospheres
l Protective coatings against scaling of conventional low alloy steels
0Cr23Al5 is a ferritic iron-chromium-aluminum alloy(FeCrAl alloy) for use in arc and flame spray systems. The alloy produces dense, well-bond coating, resistance to high-temperature oxidation and corrosion.
Chemical Compositon of 0Cr23Al5: FeCrAl is a high-resistivity iron-chromium-aluminium alloys for use up to 1400º C (2550º F). With the well-bonding coating and high temperature oxidation resistance. So they can use in variety of industry.
They can equivalent to: TAFA Alcro PMET731
Typical Uses and Applications
Applications where good corrosion and oxidation Resistance is required
Applications for wear resistance such as erosion and abrasion
Machine element repair and restoration
Resistance to chloride-ion attack in marine environments
As a replacement for hard chrome plating
Bond coats in high-temperature coating systems
l Protective coatings against sulphur-containing atmospheres
l Protective coatings against scaling of conventional low alloy steels
0Cr23Al5 is a ferritic iron-chromium-aluminum alloy(FeCrAl alloy) for use in arc and flame spray systems. The alloy produces dense, well-bond coating, resistance to high-temperature oxidation and corrosion.
| Cr | Si | Mn | Cr | Al | Fe | |
| Nominal composition | Bal. | |||||
| Min(%) | 20.5 | 5.3 | ||||
| Max(%) | 0.080 | 0.7 | 0.4 | 23.5 | 6.3 |
Performance Properties:
| Wire Size | Yield Strength | Tensile Strength | Elongation |
| diameter | Rp0.2 | Rm | A |
| mm | MPa | MPa | % |
| 1.6 | 830 | 930 | 5 |
Typical Deposit Characterstics:
| Deposit Efficiency(%) | 62-78 |
| Hardness HV (300g) | 165-280 |
| Surface roughness(um) | 11-16 |
| Porosity(%) | 1-6* |
| Oxides(%) | 5-20* |